Medium-durometer tin-cure RTV-2 case mold silicone

General Information

GI-1032 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for making case molds for the china and ceramics industries. GI-1032 is also excellent for casting polyurethane foam parts when a slightly higher hardness is desired. GI-1032 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can be accelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1032 is extremely useful for those applications where a medium durometer is required.

Typical Properties

Uncatalyzed Compound

Color

Base:WhiteActivator:Green or Blue

Viscosity

Base:65,000–85,000cpsActivator:300–400cps

Mixing Ratio

By weight:100:10By volume:100:11.4

Mixed Viscosity

40,000–50,000cps

Working Time

1.5–2.5hours

Cure Time

16–18hours

Shelf Life

6months

Vulcanized (Cured) Properties

Measured at 7 days, 70°F / 50% relative humidity

Shore A Hardness

One day:307 days:36

±4 durometer

Tear Resistance

100 ± 15ppiASTM D624

Tensile Strength

525 ± 25psiASTM D412

Elongation

275 ± 25%ASTM D412

Service Temperature

-60 to 350°F

Shrinkage

0.10%

Specific Gravity

1.13

Coverage

24.5in³ / lb